| SABIC Innovative Plastics Lexan? 103R PC | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polycarbonate (PC) | ||
| Material Notes: | UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 7.0 MFR, for thicker sections without sinks. UV Stabilized for outdoor and lighting. Internal mold release. | ||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 | ||
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D792 | ||
| Water Absorption |
0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 | ||
|
0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D570 | ||
| Linear Mold Shrinkage, Flow |
0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow |
7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 70 | 70 | ASTM D785 | ||
| Hardness, Rockwell R | 118 | 118 | ASTM D785 | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 | ||
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Izod Impact, Notched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 | ||
| Tensile Impact Strength | 546 kJ/m2 | 260 ft-lb/in2 | Type S; ASTM D1822 | ||
| Dart Drop, Total Energy | 169 J | 125 ft-lb | ASTM D3029 | ||
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 | ||
|
Dielectric Constant
|
2.96 @Frequency 1.00e+6 Hz |
2.96 @Frequency 1.00e+6 Hz |
ASTM D150 | ||
|
3.17 @Frequency 50.0 - 60.0 Hz |
3.17 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |||
| Dielectric Strength |
14.9 kV/mm @Thickness 3.20 mm |
378 kV/in @Thickness 0.126 in |
in air; ASTM D149 | ||
|
Dissipation Factor
|
0.00090 @Frequency 50.0 - 60.0 Hz |
0.00090 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | ||
|
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A | ||
| Hot Wire Ignition, HWI | 7.0 - 15 sec | 7.0 - 15 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow |
68.4 μm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 μin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | ||
| Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C351 | ||
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft2-°F | ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) |
137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) |
132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Vicat Softening Point | 154 °C | 309 °F | Rate B/50; ASTM D1525 | ||
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B | ||
| Flammability, UL94 |
HB @Thickness 0.760 mm |
HB @Thickness 0.0299 in |
UL 94 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.586 | 1.586 | ASTM D542 | ||
| Haze |
1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 | ||
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 | ||
|
De |
|||||
| Specific Volume | 0.83cm^3/g | ASTM D792 | |||
| UV-light, water exposure/immersion | F1 | UL 746C | |||